This paper aims to design the nano-titanium dioxide (TiO₂) coating system which has superhydrophilic property, self-cleaning mechanism and antifog property as well as strong adhesion on glass substrate.

Two hydrophilic materials have been used such as TiO₂ nanoparticles as fillers and hydrophilic copolymer, Pluronic F-127 by using simple sol–gel approach. The prepared solution was applied onto glass through dip- and spray-coating techniques and then left for drying at ambient temperature.

The nano-TiO₂ superhydrophilic coating has achieved the water contact angle of 4.9° ± 0.5°. The superhydrophilic coating showed great self-cleaning effect against concentrated syrup and methylene blue where thin layer of water washes the dirt contaminants away. The nano-TiO₂ coating exhibits great antifog performance that maintains high transparency of around 89% when the coated glass is placed above hot-fog vapor for 10 min. The fog droplets were condensed into water film which allowed the transmission of light through the glass. The strong adhesion of coated glass shows no total failure at scratch profile when impacted with scratch load of 500, 800 and 1,200 mN.

Findings will be useful in the development of self-cleaning superhydrophilic coating that is applicable on building glass and photovoltaic panel.

The developed nano-TiO₂ coating is developed by the combination of hydrophilic organic copolymer–inorganic TiO₂ network to achieve great superhydrophilic property, optimum self-cleaning ability and supreme antifog performance.

The findings will be useful for residents in building glass window where the application will reduce dust accumulation and keep the glass clean for longer period.

The synthesis of nano-TiO₂ superhydrophilic coating which can be sprayed on large glass panel and cured at ambient temperature.

The purpose of this study is to develop anti-corrosion coating systems using disposable waste materials. The dissolved polyethylene terephthalate (PET) has been blended with epoxy resin and stoichiometrically cured with a polyamide resin.

Glycolysis process was found to be the most optimum candidate to dissolve PET. The developed coating systems were characterized by Fourier transform infrared spectroscopy for confirmation of the molecular bonding structures. The mechanical properties were characterized by performing pull-off test and cross hatch test for mechanical properties on the coated panel. Also, the glossiness test was used by reflecting light on the coated surface. The corrosion protection performance of the coated mild steel panels was examined using electrochemical impedance spectroscopy. Furthermore, the wettability of the developed coating systems was evaluated by using water contact angle technique.

It was observed that the coating system which contains 10 per cent of dissolved PET (S2) showed the highest adhesion and corrosion protection properties.

Recyclable PET bottles have outstanding chemical properties, adhesion properties, low cost, low permeability to gases and solvents making it suitable as a coating with superior barrier properties.

This paper aims to fabricate a polymer-based polyethylene glycol (PEG) coating with acrylic resin as a binder that can show antiviral activity against the feline coronavirus (FCov) on the glass substrate.

The PEG/acrylic coating systems of different weight percentages were coated on the glass substrates using the spray-coating method and cured at room temperature for 24 h.

The coating system containing 20 Wt.% of PEG exhibits the highest antiviral activities as high as 99.9% against FCov compared with other samples.

Findings will be useful in the development of antiviral coating for PPE fabrics by using the simple synthesis method.

Application of PEG as an antiviral agent in the antiviral coating system with high antiviral activities about 99.9%.

The purpose of this study is to develop a protective coating system on mild steel panel incorporating epoxidized natural rubber with acrylic polyol resin.

In this work, a novel attempt is made to develop binder coatings using epoxidized natural rubber-based material and an organic resin (acrylic resin) for corrosion protection on metal substrate. Seven different samples of multifunctional coatings are developed by varying the compositions of epoxidized natural rubber (ENR) and acrylic resin. The properties of the developed coatings have been characterized using analytical methods such as Fourier transform infrared spectroscopy (FTIR) and electrochemical impedance spectroscopy (EIS). EIS has been carried out for 30 days to evaluate the corrosion resistance after immersing into 3.5 wt.% of sodium chloride. Cross hatch cut tester (CHT) has been used to study the adhesive properties. UV–Visible Spectroscopy (UV–Vis) was also used to assess changes in the coating-film transparency of the natural rubber-based coating systems in this study.

The developed coatings have formed uniform layer on the substrate. CHT results show excellent adhesion of the coatings. Higher concentrations of ENR have higher transparency level, which reduces when the acrylic concentration increases. FTIR analysis confirms the crosslinking that occurred between the components of the coatings. Based on the impedance data from EIS, the incorporation of natural rubber can be an additive for the corrosion protection, which has the coating resistance values well above 108Ω even after 30 days of immersion.

The blending method provides a simple and practical solution to improve the strength and adhesion properties of acrylic polyol resin with epoxidized natural rubber. There is still improvement needed for long-term applications.

The work has been conducted in our laboratory. The combination of natural rubber-based materials and organic resins is a new approach in coating research.

There is a strong inducement to develop new inorganic materials to substitute the current industrial pigments, which are known for their poor ultraviolet absorbent and low photoluminescence (PL) properties. The purpose of this paper is to invent a better rare-earth-based pigment material as a spectral modifier with good luminescence properties to enhance the spectral response for photovoltaic panel application.

Different phosphor samples made of nano-calcium carbonate (CaCO₃) with varied wt.% of the dopant Dysprosium doped calcium borophosphate (CBP/Dy) as (W0 – 0%, W1 – 3,85%, W2 – 7.41%, W3 –10.71% and W4 –13.79%) were prepared via the solid-state diffusion method at 600 °C for 6 h using a muffle furnace. The structural, morphological and luminescence properties of the CaCO₃:CBP/Dy powder samples were examined using scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and PL test.

The XRD, SEM and FTIR results verified the crystalline formation, morphological behaviour and vibration bonds of synthesized CBP/Dy-doped CaCO₃ powder samples. XRD pattern revealed that the synthesized powder samples exhibit crystalline structured materials, and SEM results showed irregular shape and porous-like structured morphologies. FTIR spectrum shows prominent bands at 712, 874 and 1,404 cm⁻¹, corresponding to asymmetric stretching vibrations of CO3²⁻ groups and out-of-plane bending. PL characterization of CBP/Dy-doped CaCO₃ (sample W) shows emission at 427 nm (λmax) under the excitation of 358 nm. The intensity of PL emission spectra drops due to the concentration quenching effect, while the maximum PL intensity is observed in the W3 phosphor powder system.

This phosphor powder is expected to find out the potential application such as a spectral modifier which is applied to match the energy of photons with solar cell bandgap to improve spectral absorption and lead to better efficiency.

The introduction of a nano-CaCO₃:CBP/Dy hybrid powder system with good luminescence properties to be used as spectral modifiers for solar cell application has been synthesized in the lab, which is a novel attempt.

The purpose of this paper is to introduce the simple synthesis process of thermal-insulation coating by using three different nanoparticles, namely, nano-zinc oxide (ZnO), nano-tin dioxide (SnO₂) and nano-titanium dioxide (TiO₂), which can reduce the temperature of solar cells.

The thermal-insulation coating is designed using sol-gel process. The aminopropyltriethoxysilane/methyltrimethoxysilane binder system improves the cross-linking between the hydroxyl groups, -OH of nanoparticles. The isopropyl alcohol is used as a solvent medium. The fabrication method is a dip-coating method.

The prepared S1B1 coating (20 Wt.% of SnO₂) exhibits high transparency and great thermal insulation property where the surface temperature of solar cells has been reduced by 13°C under 1,000 W/m² irradiation after 1 h. Meanwhile, the Z1B2 coating (20 Wt.% of ZnO) reduced the temperature of solar cells by 7°C. On the other hand, the embedded nanoparticles have improved the fill factor of solar cells by 0.2 or 33.33%.

Findings provide a significant method for the development of thermal-insulation coating by a simple synthesis process and low-cost materials.

The thermal-insulation coating is proposed to prevent exterior heat energy to the inside solar panel glass. At the same time, it can prevent excessive heating on the solar cell’s surface, later improves the efficiency of solar cell.

This study presents a the novel method to develop and compare the thermal-insulation coating by using various nanoparticles, namely, nano-TiO₂, nano-SnO₂ and nano-ZnO at different weight percentage.

This paper introduced the simple synthesis process of self-cleaning coating with fog-resistance property using hydrophobic polydimethylsiloxane (PDMS) polymer and nano-calcium carbonate (nano-CaCO₃) and titanium dioxide (TiO₂).

The synthesis method of PDMS/nano-CaCO₃-TiO₂ is based on sol-gel process. The crosslinking between PDMS and nanoparticles is driven by the covalent bond at temperature of 50°C. The 3-Aminopropyltriethoxysilane is used as binder for nanoparticles attachment in polymer matrix. Two fabrication methods are used, which are dip- and spray-coating methods.

The prepared coated glass fulfilled the requirement of standard self-cleaning and fog-resistance performance. For the self-cleaning test BS EN 1096-5:2016, the coated glasses exhibited the dust haze value around 20%–25% at tilt angle of 10°. For the antifog test, the coated glasses showed the fog haze value were below 2% and the gloss value were above 85%. The obtained results completely achieved the standard antifog value ASTM F659-06 protocol.

Findings will provide an infrastructure support for the building glass to enhance building’s energy efficiency, cleaning performance and friendly environment.

This study proposed the simple synthesis method using hydrophobic polymer and nano-CaCO₃ and nano-TiO₂, which can achieve optimum self-cleaning property at low tilt angle and fog-resistance performance for building glass.

The research findings have high potential for building company, cleaning building company and government sector. The proposed project capable to reduces the energy consumption about 20% per annum due to labor cost, time-consuming and safety during manual cleaning.

The novel method to develop self-cleaning coating with fog-resistance using simple synthesis process and fabrication method for building glass application.

This paper aims to investigate the thermal stability and hydrophobicity of difference alkyl chain of silanes with silicon (Si) micro- and nanoparticles.

Sol-gel methods have been used to design superhydrophobic glass substrates through surface modification by using low-surface-energy Isooctyl trimethoxysilane (ITMS) and Ethyl trimethoxysilane (ETMS) solution. Hierarchical double-rough scale solid surface was built by Si micro- and nanoparticles to enhance the surface roughness. The prepared sol was applied onto glass substrate using dip-coating method and was dried at control temperature of 400°C inside the tube furnace.

The glass substrate achieved the water contact angle as high as 154 ± 2° and 150.4 ± 2° for Si/ITMS and Si/ETMS films, respectively. The Si/ITMS and Si/ETMS also were equipped with low sliding angle as low as 3° and 5°, respectively. The Si micro- and nanoparticles in the coating system have created nanopillars between them, which will suspend the water droplets. Both superhydrophobic coatings have showed good stability against high temperature up to 200°C as there are no changes in WCA shown by both coatings. Si/ITMS film sustains its superhydrophobicity after impacting with further temperature up to 400°C and turns hydrophobic state at 450°C.

Findings will be useful to develop superhydrophobic coatings with high thermal stability.

Sol method provides a suitable medium for the combination of organic-inorganic network to achieve high hydrophobicity with optimum surface roughness.

Application of different alkyl chain groups of silane resin blending with micro- and nanoparticles of Si pigments develops superhydrophobic coatings with high thermal stability.

The paper aims to investigate the effect of Degussa P-25 Titanium Dioxide (TiO₂) nanoparticles on hydrophobicity and self-cleaning ability as a single organic coating on glass substrate.

Two methods have been used to enhance the hydrophobicity on glass substrates, namely, surface modification by using low surface energy isooctyltrimethoxysilane (ITMS) solution and construction of rough surface morphology using Degussa P-25 TiO₂ nanoparticles with simple bottom-up approach. The prepared sol was applied onto glass substrate using dip-coating technique and stoved in the vacuum furnace 350°C.

The ITMS coating with nano TiO₂ pigment has modified the glass substrate surface by achieving the water contact angle as high as 169° ± 2° and low sliding angle of 0° with simple and low-cost operation. The solid and air phase interface has created excellent anti-dirt and self-cleaning properties against dilute ketchup solution, mud and silicon powder.

Findings will be useful in the development of self-cleaning and anti-dirt coating for photovoltaic panels.

Sol method provides the suitable medium for the combination of organic–inorganic network to achieve high superhydrophobicity and optimum self-cleaning ability.

Application of blended organic–inorganic sol as self-cleaning and anti-dirt coating film.

The purpose of this paper is to implement coating system by varying the amount of nano-sized titanium dioxide, (nano-TiO₂) combined with various organic binders and to study the coating effects on the performance of solar cell in terms of temperature and efficiency.

Nano-TiO₂ coatings are developed in two types of binder networks; the combination of methyltrimethoxy silane (MTMS) and nitric acid and the combination of 3-aminopropyl triethoxysilane (APTES) and MTMS. Overall, the formulations method was cost-effective, produces good transparency, clear and managed to dry at room temperature. The coating mixtures were applied onto the glass substrate by using the dip-coating method and the coated substrate were sent for several characterizations.

This study demonstrated that TiO₂ nanoparticle coating in APTES/MTMS matrix showed a thermal-decreasing result on solar cells, where the cell temperature is reduced to 46.81°C (T₂ coating type) from 55.74°C (without coating) after 1-h exposure under 1,000 W/m² irradiance in a solar simulator. Contrary to prior works where solar cell coatings were reported to reduce the cell temperature at the expense of the cell efficiency, the results from this study reported an improved fill factor (FF) of solar cells. From the photovoltaic (PV) characteristics study, the FF for solar cells is increased by approximately 0.2, i.e. 33.3 per cent, for all coatings compared to the non-coated cell.

Findings will be able to contribute in the development of temperature-reducing and efficiency-enhancing coating for PV panels.

A simple dip-coating method provides an even distribution of TiO₂ nanoparticle coating on the glass panel, which is cost-effective and time-efficient to reduce the temperature of solar cell while maintaining its efficiency.

The ability of nano-TiO₂ coatings with a simple fabrication method and the right solution to reduce the surface temperature of solar cells while improving the FF of the cells.